Introduction

XR- Silicone PUTTY is new silicone compounds (platinum catalyst) that can be easily mixed and applied by hand to a variety of surfaces. Silicone Putty is mixed in equal amounts (1A:1B) by volume/weight.MC-P35 has a pot life of about 5-20minute with a cure time of about 30-60 min at room temperature (73°F/23°C). Shrinkage is low and cured rubber is exceptionally strong (very high tensile strength), durable and will resist high temperatures (for casting low-temperature melt metal alloys). They also resist cure inhibition.MC-P35 are also FOOD SAFE and can be used for culinary applications.

Features
-Easy to use, 3 Minute working time, 25 minute cure.
-Ideal for small molds, excellent detail from original.
-Strong, flexible, reusable molds.
-High Heat range, up to 400o F.
-No Shrinkage.
-Self releasing, no mold release agent required for most applications.
-Odorless, Non Toxic. FDA Compliant, Food Grade.

Technical Overview

Applications

Applications include making fast mold impressions from almost any surface, orthotics / orthopedic, equine hoof repair, jewelry making and more.

Usage Instruction

1. Under the room temperature, take the same amount of base component

(blue) and catalyst component (white).

2. Mix the two components together. It is recommended to use the blue spoon to take part B and white spoon to take part A.

3. Use your fingertips to mix the two components completely.

4. Close the lid immediately after usage, the cover can not be interchanged.

Precautions

1. Do not use natural rubber gloves. It is recommended to use disposable polyethylene plastic gloves.

2. The product contains platinum catalyst, sulfur, phosphorus, amine, etc. will slow down or even stop the curing reaction, and thus it must avoid sulfur, phosphorus, amine, acrylic and meth acrylic acid esters and other chemical products in use.

3. Close the lid tightly and immediately after use, keep it in cool place, and be refrigerated in summer.

4. The temperature has a significant impact on the curing time; the curing reaction will slow down at low temperature, and speed up at high temperature curing speed. It should adjust operation rhythm according to the environment and the finger temperature.

5. It is strictly recommended to use the same amount of base and catalyst. Unequal amount will lead to delayed or accelerated cure.

6. Avoid contact with water, water will make the material deteriorated.