Silicone Putty for Dental Molds is a hydrophilic addition silicone rubber impression material, it contains two components, Part A is platinum catalyst, and Part B is hydrogen containing polysiloxane. This product comprises liquid material and powder material. The main raw material is a silicone oil, silicone resin, alumina, quartz powder and etc.
Composition
Base components 350 g;
Catalyst component 350 g;
A white spoon;
A blue spoon
Physical Properties:
Before Curing |
Catalyst Components |
Base Components |
Appearance |
White putty |
Blue putty |
Mix ratio |
1:1 |
|
Pot life |
> 60 seconds |
|
Curing time(37C) |
< 5 min |
|
After Curing |
||
Hardness(Shore A) |
60 |
|
Permanent deformation % |
<0.2% |
|
Dimensional stability % |
<0.25 |
|
Copy details(μm) |
<1.5 |
|
Tearing Strength Mpa |
2.0 |
|
Temperature stability |
60°C for 1 week |
|
Elongation% |
267 |
Application
It is suitable for the production of precise dental crown, dental fixed bridge, dentures, and articulation registration and takes the mold of oral tissue
Usage Instruction
1. Under the room temperature, take the same amount of base component (blue) and catalyst component (white).
2. Mix the two components together. It is recommended to use the blue spoon to take the base component and white spoon to take catalyst component.
3. Use your fingertips to mix the two components together and knead for at least 30 seconds until they are mixed completely.
4. Close the lid immediately after usage, the cover can not be interchanged.
Main Feature
1. Good plasticity, small volume incorporation rate, it needs only 3-5min to vulcanize into elastomer at oral temperature, very easy to remove from the mouth after the stamp, and has good chemical stability.
2. High accuracy of mold impression, capability of reproducing the fine structure of the mouth, with good elastic recovery, and good tear strength and dimensional stability, it can provide accurate and reliable morphological basis for clinical dentistry.
3. It has compatibility with almost all model materials, reusable for a period of time and can be sterilized.
Precautions
1. Do not use natural rubber gloves. It is recommended to use disposable polyethylene plastic gloves.
2. The product contains platinum catalyst, sulfur, phosphorus, amine, etc. will slow down or even stop the curing reaction, and thus it must avoid sulfur, phosphorus, amine, acrylic and meth acrylic acid esters and other chemical products in use.
3. Close the lid tightly and immediately after use, keep it in cool place, and be refrigerated in summer.
4. The temperature has a significant impact on the curing time; the curing reaction will slow down at low temperature, and speed up at high temperature curing speed. It should adjust operation rhythm according to the environment and the finger temperature.
5. It is strictly recommended to use the same amount
of base and catalyst. Unequal amount will lead to delayed or accelerated cure.